Description
Specifications
polymeric PVC for partial application. Designed for wrapping smooth surfaces or elements of medium difficulty in wrapping; spoilers, mirrors, etc.
The thickness of film:Â 0.13mm
The thickness of film with release liner:Â 0.29mm
Type of film:Â High grade polymeric calendered vinyl film with air release channels
Colors:Â Black
Series:Â 180 series
Adhesive: Henkel solvent-based acrylic adhesive, transparent, ultra-weather-resistant, viscosity 1000~3000cps, thickness 12 μm dry
Release liner:Â Felix Schoeller Release Liner / 20-104-20-1,9 printed, double side PE coated Kraft. One side solventless silicone-coated, air release (ISO 9001, ISO 140001, OHSAS 18001)
Storing period: 2 years if stored in +10°С to +20°С, relative humidity 50%, in original package, away from direct sunlight, clean and dry place.
Indoor life: 3Â years when followed rules of application and use
Outdoor life: 2Â years when followed rules of application and use
Application: from +5°С to +30°С, usage from -30°С to +50°С
Dimensional stability:Â shrinkage less than 2%
Plastification: between 28%-38%
Breaking Strength:Â 23.7 N/10mm (Average) Test Method: ASTM D3759/D3759M-05 6.4 N/10mm (Average) Test Method: ASTM D3330/D3330-04
Light Ageing in UV Exposure: Test Method: ASTM D4329-13 Cycle A & ISO 105-A02:1993/Cor.2:2005, Test result: 3-4 Exposure cycle: ASTM D4329-13 cycle A, Lamp type: UVA-340 8h UV at (60±2.5)℃ BPT, 0.89 W/ (m2•nm)@340nm, 4h condensation at (50±2.5)℃ BPT, Exposure duration: 44h
Post-heating: 95 Celsius
Package:Â Roll width is 152, length 18Â m, weight 14 kg